Investigation of fatigue behavior using surface shot peened technique for 2024-t4 al-alloy
The strength and fatigue lifetime of AL alloy 2024-T4 were estimated using flat fatigue specimen and stress ratio R=-1 at room temperature (RT). After fatigue testing,it was found that both fatigue region (low cycle fatigue and high cycle fatigue) was improved after the shoot penning of the surface...
Saved in:
| Published in: | The Iraqi journal for mechanical and materials engineering. Vol. 16; no. 2; pp. 129 - 142 |
|---|---|
| Main Authors: | , , |
| Format: | Journal Article |
| Language: | Arabic English |
| Published: |
Babylon, Iraq
University of Babylon, College of Engineering
2016
|
| Online Access: | Get full text |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | The strength and fatigue lifetime of AL alloy 2024-T4 were estimated using flat fatigue specimen and stress ratio R=-1 at room temperature (RT). After fatigue testing,it was found that both fatigue region (low cycle fatigue and high cycle fatigue) was improved after the shoot penning of the surface .This improvement appeared due to the compressive residual stress established at the shoot penned surface . Also, the fatigue life improvement factor was obtained around (6) while the fatigue strength factor was found to be around 26.
KEYWORDS :-
2024-T4 Al-alloy, fatigue, life and strength, shot peening |
|---|---|
| ISSN: | 2076-1819 2313-3783 |