NH_3-SCR denitration catalyst performance over vanadium-titanium with the addition of Ce and Sb
Selective catalytic reduction technology using NH3 as a reducing agent（NH3-SCR） is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray di...
Saved in:
| Published in: | 环境科学学报：英文版 no. 5; pp. 74 - 80 |
|---|---|
| Main Author: | |
| Format: | Journal Article |
| Language: | English |
| Published: |
2015
|
| Subjects: | |
| Online Access: | Get full text |
| Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
| Summary: | Selective catalytic reduction technology using NH3 as a reducing agent（NH3-SCR） is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray diffractometer（XRD）, Brunauer-Emmett-Teller（BET）, Transmission electron microscopy（TEM）, Fourier transform infrared spectroscopy（FT-IR）, UV-Vis diffuse reflectance spectroscopy（UV-Vis DRS）, Raman and Hydrogen temperature-programmed reduction（H2-TPR）. The catalytic activities of V5 CexS by/TiO2 catalysts for denitration were investigated in a fixed bed flow microreactor. The results showed that cerium, vanadium and antimony oxide as the active components were well dispersed on TiO2, and the catalysts exhibited a large number of d-d electronic transitions, which were helpful to strengthen SCR reactivity. The V5 CexS by/TiO2 catalysts exhibited a good low temperature NH3-SCR catalytic activity. In the temperature range of 210 to 400℃, the V5 CexS by/TiO2 catalysts gave NO conversion rates above 90%. For the best V5Ce35Sb2/TiO2 catalyst, at a reaction temperature of 210℃, the NO conversion rate had already reached 90%. The catalysts had different catalytic activity with different Ce loadings. With the increase of Ce loading, the NO conversion rate also increased. |
|---|---|
| Bibliography: | Chi Xu, ,jian Liu, Zhen Zhao, Fei Yu, Kai Cheng Yuechang Wei, Aijun Duan, Guiyuan jiang（ 1. State Key Laboratory of Heavy Oil, China University of Petroleum, Beijing 102249, China.2. Department of Agricultural and Biological Engineering, Mississippi State University, 130 Creelman St, Mississippi State, MS 39762, United States） VCeSb/TiO2 catalyst SCR Denitration Low temperature N2 selectivity Selective catalytic reduction technology using NH3 as a reducing agent（NH3-SCR） is an effective control method to remove nitrogen oxides. TiO2-supported vanadium oxide catalysts with different levels of Ce and Sb modification were prepared by an impregnation method and were characterized by X-ray diffractometer（XRD）, Brunauer-Emmett-Teller（BET）, Transmission electron microscopy（TEM）, Fourier transform infrared spectroscopy（FT-IR）, UV-Vis diffuse reflectance spectroscopy（UV-Vis DRS）, Raman and Hydrogen temperature-programmed reduction（H2-TPR）. The catalytic activities of V5 CexS by/TiO2 catalysts for denitration were investigated in a fixed bed flow microreactor. The results showed that cerium, vanadium and antimony oxide as the active components were well dispersed on TiO2, and the catalysts exhibited a large number of d-d electronic transitions, which were helpful to strengthen SCR reactivity. The V5 CexS by/TiO2 catalysts exhibited a good low temperature NH3-SCR catalytic activity. In the temperature range of 210 to 400℃, the V5 CexS by/TiO2 catalysts gave NO conversion rates above 90%. For the best V5Ce35Sb2/TiO2 catalyst, at a reaction temperature of 210℃, the NO conversion rate had already reached 90%. The catalysts had different catalytic activity with different Ce loadings. With the increase of Ce loading, the NO conversion rate also increased. 11-2629/X |
| ISSN: | 1001-0742 1878-7320 |