Excellent combination of compressive strength and ductility of (CoCrFeNi)x(Co0.26Cr0.07Fe0.16Ni0.31Hf0.4) high-entropy alloys

• Published in: Materials & design Vol. 202; p. 109569
• Main Authors: Xie, Tongbin, Xiong, Zhiping, Liu, Zhe, Deng, Guanyu, Cheng, Xingwang
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 01-04-2021; Elsevier
• Subjects: Enthalpies; Eutectic; Hafnium; Laves; Laves; Eutectic; Hafnium; Enthalpies
• ISSN: 0264-1275; 1873-4197
• DOI: 10.1016/j.matdes.2021.109569

Instead of conventional CoCrFeNiHfx high-entropy alloys (HEAs), we investigated the evolution of microstructure and compressive mechanical properties of (CoCrFeNi)x(Co0.26Cr0.07Fe0.16Ni0.31Hf0.4) HEAs with varying x. Increasing x from 0.5 to 1.0, the microstructure changes from hyper-eutectic ones consisting of primary Laves phase and eutectic structure (x < 0.7), firstly to eutectic ones consisting of alternative FCC and Laves phase (x = 0.7 and 0.8), and finally to hypo-eutectic ones consisting of primary FCC phase and eutectic structure (x > 0.8). Interestingly, two different morphologies of eutectic microstructures are observed when x = 0.7 and 0.8 probably due to different fusion entropies of each phase. Increasing x from 0.5 to 1.0 reduces the yield strength from 1661 ± 64 to 688 ± 17 MPa but enhances the compressive ductility due to an increased fraction of soft FCC phase from ~0.39 to ~0.74. The second phase strengthening is the main strengthening mechanism. Importantly, when x = 0.9 and 1.0, these two alloys are not fractured when the strain reaches 0.5, one of which shows a large yield strength of 1028 ± 45 MPa (x = 0.9). Compared with conventional CoCrFeNiHfx, the studied HEAs exhibit a much better combination of compressive strength and ductility.
[Display omitted]
•(CoCrFeNi)x(Co0.26Cr0.07Fe0.16Ni0.31Hf0.4) microstructure changes from hyper-eutectic to hypo-eutectic with x increase.•Eutectic point is simultaneously obtained when x = 0.7 and x = 0.8 of (CoCrFeNi)x(Co0.26Cr0.07Fe0.16Ni0.31Hf0.4).•The eutectic microstructure changes from irregular lamella to regular lamella when increasing x value.•(CoCrFeNi)x(Co0.26Cr0.07Fe0.16Ni0.31Hf0.4) have a better combination of compressive strength and ductility than CoCrFeNiHfx.