Bond strengths of various resin cements to different ceramics

• Published in: Brazilian oral research Vol. 33; p. e095
• Main Authors: FARIAS, David Cardoso Sandes, GONÇALVES, Letícia Machado, WALTER, Ricardo, CHUNG, Yunro, BLATZ, Markus Bernhard
• Format: Journal Article
• Language: English
• Published: Sociedade Brasileira de Pesquisa Odontológica - SBPqO 01-01-2019; Sociedade Brasileira de Pesquisa Odontológica
• Subjects: Aging; Aluminum Oxide; Ceramics; Dentistry; DENTISTRY, ORAL SURGERY & MEDICINE; Resin Cements; Shear Strength; Aging; Resin Cements; Shear Strength; Aluminum Oxide; Ceramics
• ISSN: 1806-8324; 1807-3107; 1807-3107
• DOI: 10.1590/1807-3107bor-2019.vol33.0095

Abstract This study evaluates the shear bond strength (SBS) of various resin cements to different ceramics. Composite resin cylinders of Z100 were fabricated and cemented to disks of feldspathic ceramic (Creation), leucite-reinforced feldspathic ceramic (Empress I), and densely sintered aluminum oxide ceramic (Procera AllCeram) using five resin cements: Panavia F (PAN), RelyX ARC (ARC), RelyX Unicem (RXU), RelyX Veneer, and Variolink II. SBS was measured after three days of water storage (baseline) and after artificial aging (180 days of water storage along with 12,000 thermal cycles). Failure mode of fractured specimens also was evaluated. Data were analyzed with Kruskal-Wallis and Mann-Whitney tests (α=0.05). RXU showed 1) the lowest baseline median SBS to feldspathic ceramic, which was not statistically different from PAN; 2) the lowest median baseline SBS to leucite-reinforced feldspathic and densely sintered aluminum-oxide ceramics. All cements performed similarly after aging, except for ARC (median 0.0 MPa) and PAN (median 16.2 MPa) in the densely sintered aluminum-oxide ceramic group. Resin cements perform differently when bonded to different ceramic substrates. While all test resin cements worked similarly in the long-term to feldspathic and leucite-reinforced feldspathic ceramics, only the MDP-containing resin cement provided durable bonds to densely sintered aluminum-oxide ceramic.