Tailoring of physical properties in highly filled experimental nanohybrid resin composites

• Published in: Dental materials Vol. 27; no. 7; pp. 664 - 669
• Main Authors: Pick, Bárbara, Pelka, Matthias, Belli, Renan, Braga, Roberto R, Lohbauer, Ulrich
• Format: Journal Article
• Language: English
• Published: England Elsevier Ltd 01-07-2011
• Subjects: Advanced Basic Science; Analysis of Variance; Bisphenol A-Glycidyl Methacrylate - chemistry; Ceramics - chemistry; Composite Resins - chemistry; Density; Dental Marginal Adaptation; Dental Stress Analysis; Dentistry; Elastic Modulus; Fillers; Linear Models; Materials Testing; Molecular Weight; Nanocomposites; Nanocomposites - chemistry; Nanomaterials; Nanoparticles; Nanostructure; Organically Modified Ceramics; Particle Size; Polyethylene Glycols - chemistry; Polymer matrix composites; Polymerization; Polymerization shrinkage; Polymethacrylic Acids - chemistry; Resin composite; Shrinkage; Shrinkage stress; Silanes - chemistry; Silicon Dioxide - chemistry; Statistics, Nonparametric; Stress, Mechanical; Nanoparticles; Elastic modulus; Resin composite; Shrinkage stress; Polymerization shrinkage
• ISSN: 0109-5641; 1879-0097
• DOI: 10.1016/j.dental.2011.03.007

Abstract Objectives To assess the elastic modulus (EM), volumetric shrinkage (VS), and polymerization shrinkage stress (PSS) of experimental highly filled nanohybrid composites as a function of matrix composition, filler distribution, and density. Methods One regular viscosity nanohybrid composite (Grandio, VOCO, Germany) and one flowable nanohybrid composite (Grandio Flow, VOCO) were tested as references along with six highly filled experimental nanohybrid composites (four Bis-GMA-based, one UDMA-based, and one Ormocer® -based). The experimental composites varied in filler size and density. EM values were obtained from the “three-point bending” load–displacement curve. VS was calculated with Archimedes’ buoyancy principle. PSS was determined in 1-mm thick specimens placed between two (poly)methyl methacrylate rods ( Ø = 6 mm) attached to an universal testing machine. Data were analyzed using oneway ANOVA, Tukey's test ( α = 0.05), and linear regression analyses. Results The flowable composite exhibited the highest VS and PSS but lowest EM. The PSS was significantly lower with Ormocer. The EM was significantly higher among experimental composites with highest filler levels. No significant differences were found between all other experimental composites regarding VS and PSS. Filler density and size did not influence EM, VS, or PSS. Significance Neither the filler configuration nor matrix composition in the investigated materials significantly influenced composite shrinkage and mechanical properties. The highest filled experimental composite seemed to increase EM by keeping VS and PSS low; however, matrix composition seemed to be the determinant factor for shrinkage and stress development. The Ormocer, with reduced PSS, deserves further investigation. Filler size and density did not influence the tested parameters.