Effects of Post-Curing Light Intensity on the Mechanical Properties and Three-Dimensional Printing Accuracy of Interim Dental Material

• Published in: Materials Vol. 15; no. 19; p. 6889
• Main Authors: Kang, Min-Jung, Lim, Jung-Hwa, Lee, Chan-Gyu, Kim, Jong-Eun
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 04-10-2022; MDPI
• Subjects: 3D printing; additive manufacturing; CAD/CAM; Curing; Dental materials; Diamond pyramid hardness; flexural strength; Luminous intensity; Manufacturing; Mechanical properties; post-curing; Rapid prototyping; Software; Spectrum analysis; Three dimensional printing; Vickers microhardness; South Korea; United States > US; Japan; Vickers microhardness; additive manufacturing; flexural strength; post-curing; CAD/CAM; three-dimensional printing; three-dimensional accuracy; degree of conversion
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma15196889

This study evaluated the effects of the light intensity of curing and the post-curing duration on the mechanical properties and accuracy of the interim dental material. After designing the specimen, 3D printing was performed, and the light intensity was divided into groups G20, G60, G80, and G120 (corresponding to 1.4−1.6, 2.2−3.0, 3.8−4.4, and 6.4−7.0 mW/cm2, respectively), with no post-curing or 5, 10, or 20 min of post-curing being performed. The flexural properties, Vickers microhardness, degree of conversion (DC), and 3D accuracy were then evaluated. The flexural properties and Vickers microhardness showed a sharp increase at the beginning of the post-curing and then tended to increase gradually as the light intensity and post-curing time increased (p < 0.001). On the other hand, there was no significant difference between groups in the accuracy analysis of a 3D-printed three-unit bridge. These results indicate that the light intensity of the post-curing equipment influences the final mechanical properties of 3D-printed resin and that post-curing can be made more efficient by optimizing the light intensity and post-curing time.