Effect of shot peening on the fatigue life of a Zr-based bulk metallic glass

The fatigue lives of a Zr-based bulk metallic glass (BMG) in the as-cast and shot-peened conditions were evaluated. Results suggest that shot peening does not cause significant enhancement of the fatigue performance of the BMG. Cracks were observed to nucleate in subsurface regions. This was attribu...

Full description

Saved in:
Bibliographic Details
Published in:Scripta materialia Vol. 59; no. 2; pp. 167 - 170
Main Authors: Raghavan, R., Ayer, R., Jin, H.W., Marzinsky, C.N., Ramamurty, U.
Format: Journal Article
Language:English
Published: Elsevier Ltd 01-07-2008
Subjects:
Amorphous materials
Fatigue
Fatigue life
Metallic glasses
Microcracks
Nanoindentation
Nucleation
Residual stresses
Shear bands
Shot peening
Zirconium
Zirconium base alloys
Metallic glasses
Fatigue
Residual stresses
Shear bands
Nanoindentation
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The fatigue lives of a Zr-based bulk metallic glass (BMG) in the as-cast and shot-peened conditions were evaluated. Results suggest that shot peening does not cause significant enhancement of the fatigue performance of the BMG. Cracks were observed to nucleate in subsurface regions. This was attributed to the domination of the compressive residual stress field on the surface over deformation-induced plastic flow softening that otherwise leads to easy nucleation of shear bands which act like microcracks.
Bibliography:ObjectType-Article-2
SourceType-Scholarly Journals-1
ObjectType-Feature-1
content type line 23
ISSN:1359-6462
1872-8456
DOI:10.1016/j.scriptamat.2008.03.009