Fracture Behavior of Long Fiber Reinforced Geopolymer Composites at Different Operating Temperatures

• Published in: Materials Vol. 15; no. 2; p. 482
• Main Authors: Korniejenko, Kinga, Figiela, Beata, Ziejewska, Celina, Marczyk, Joanna, Bazan, Patrycja, Hebda, Marek, Choińska, Marta, Lin, Wei-Ting
• Format: Journal Article
• Language: English
• Published: Switzerland MDPI AG 09-01-2022; MDPI
• Subjects: Bend strength; Carbon fibers; Composition; Engineering Sciences; Fiber composites; Fly ash; Geopolymers; Heating; High temperature; Long fibers; Low temperature; Mechanical properties; Metakaolin; Operating temperature; Room temperature; Sand; Temperature; Germany; fiber reinforcement; carbon fiber; glass fiber; long fiber; aramid fiber; geopolymer composite; Aramid fibers; Geopolymer composite; Glass fiber; Fiber reinforcement; Long fiber; Carbon fiber
• ISSN: 1996-1944; 1996-1944
• DOI: 10.3390/ma15020482

The aim of this article was to analyze the fracture behavior of geopolymer composites based on fly ash or metakaolin with fine aggregate and river sand, with three types of reinforcement: glass, carbon, and aramid fiber, at three different temperatures, approximately: 3 °C, 20 °C, and 50 °C. The temperatures were selected as a future work temperature for composites designed for additive manufacturing technology. The main research method used was bending strength tests in accordance with European standard EN 12390-5. The results showed that the addition of fibers significantly improved the bending strength of all composites. The best results at room temperature were achieved for the metakaolin-based composites and sand reinforced with 2% wt. aramid fiber-17 MPa. The results at 50 °C showed a significant decrease in the bending strength for almost all compositions, which are unexpected results, taking into account the fact that geopolymers are described as materials dedicated to working at high temperatures. The test at low temperature (ca. 3 °C) showed an increase in the bending strength for almost all compositions. The grounds of this type of behavior have not been clearly stated; however, the likely causes of this are discussed.