Predictive Performance of Artificial Neural Network and Multiple Linear Regression Models in Predicting Adhesive Bonding Strength of Wood

• Published in: Strength of materials Vol. 48; no. 6; pp. 811 - 824
• Main Authors: Bardak, S., Tiryaki, S., Bardak, T., Aydin, A.
• Format: Journal Article
• Language: English
• Published: New York Springer US 01-11-2016; Springer; Springer Nature B.V
• Subjects: Adhesives; Analysis; Characterization and Evaluation of Materials; Chemistry and Materials Science; Classical Mechanics; Materials Science; Neural networks; Regression analysis; Regression models; Solid Mechanics; prediction; artificial neural network; bonding strength; model comparison; multiple linear regression
• ISSN: 0039-2316; 1573-9325
• DOI: 10.1007/s11223-017-9828-x

The purpose of this study was to develop artificial neural network (ANN) and multiple linear regression (MLR) models that are capable of predicting the bonding strength of wood based on moisture content, open assembly time and closed assembly time of the joints prior to pressing process. For this purpose, the experimental studies were conducted and the models based on the experimental results were set up. As a result of the experiments conducted, it was observed that bonding strength first increased and then decreased with increasing the wood moisture content and adhesive open assembly time. In addition, the increased closed assembly time caused a decrease in bonding strength of wood. The ANN results were compared with the results obtained from the MLR model to evaluate the models’ predictive performance. It was found that the ANN model with the
R
2
value of 97.7% and the mean absolute percentage error of 3.587% in test phase exhibits higher prediction accuracy than the MLR model. The comparison results confirm the feasibility of ANN model in terms of predictive performance. Consequently, it can be said that ANN is an effective tool in predicting wood bonding strength, and quite useful instead of costly and time-consuming experimental investigations.