Evaluation of linear polymerization shrinkage, flexural strength and modulus of elasticity of dental composites

• Published in: Materials research (São Carlos, São Paulo, Brazil) Vol. 13; no. 1; pp. 51 - 55
• Main Authors: Monteiro, Gabriela Queiroz de Melo, Montes, Marcos Antonio Japiassú Resende
• Format: Journal Article
• Language: English
• Published: ABM, ABC, ABPol 01-03-2010; Associação Brasileira de Metalurgia e Materiais (ABM); Associação Brasileira de Cerâmica (ABC); Associação Brasileira de Polímeros (ABPol)
• Subjects: composite resin; ENGINEERING, CHEMICAL; flexural strength; MATERIALS SCIENCE, MULTIDISCIPLINARY; METALLURGY & METALLURGICAL ENGINEERING; modulus of elasticity; polymerization shrinkage; composite resin; flexural strength; modulus of elasticity; polymerization shrinkage
• ISSN: 1516-1439; 1980-5373; 1516-1439
• DOI: 10.1590/S1516-14392010000100012

Linear polymerization shrinkage (LPS), flexural strength (FS) and modulus of elasticity (ME) of 7 dental composites (Filtek Z350™, Filtek Z250™/3M ESPE; Grandio™, Polofil Supra™/VOCO; TPH Spectrum™, TPH3™, Esthet-X™/Denstply) were measured. For the measurement of LPS, composites were applied to a cylindrical metallic mold and polymerized (n = 8). The gap formed at the resin/mold interface was observed using scanning electron microscopy (1500×). For FS and ME, specimens were prepared according to the ISO 4049 specifications (n = 10). Statistical analysis of the data was performed with one-way ANOVA and the Tukey test. TPH Spectrum presented significantly higher LPS values (29.45 µm). Grandio had significantly higher mean values for FS (141.07 MPa) and ME (13.91 GPa). The relationship between modulus of elasticity and polymerization shrinkage is the main challenge for maintenance of the adhesive interface, thus composites presenting high shrinkage values, associated with a high modulus of elasticity tend to disrupt the adhesive interface under polymerization.