Study of Morphology and Corrosion Behavior of Aluminum Coatings on Steel Substrates under Simulated Acid Rain Conditions

• Published in: Metals (Basel ) Vol. 13; no. 3; p. 613
• Main Authors: Li, Bo, Fan, Lei, Wen, Yi, He, Jinhang, Su, Jianfeng, Zhou, Shiyuan, Liu, Shifeng, Zhang, Zhiqing
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01-03-2023
• Subjects: Acid deposition; Acid rain; Air pollution; Aluminum coatings; Carbon steel; Cathodic protection; Coatings; Corrosion; corrosion behavior; Corrosion potential; Corrosion products; Corrosion rate; Corrosion resistance; Corrosion resistant steels; Corrosion tests; Damage tolerance; Electrodes; Hydrophobic surfaces; immersion; Immersion tests (corrosion); Li Bai; Morphology; Protective coatings; salt spray; Salt spray tests; Spraying; Steel; Substrates
• ISSN: 2075-4701; 2075-4701
• DOI: 10.3390/met13030613

In this paper, aluminum coatings were prepared on a steel substrate by thermal spraying, and the corrosion morphology and corrosion resistance of the coating were investigated by salt spray and immersion tests. The results showed that after three months of salt spray tests, the coating still exhibited a surface morphology without significant damage and had good damage tolerance. Further effective protection of the substrate can be achieved by spraying the coating surface with paint. After three months of immersion test, the corrosion rate of samples with thicker coatings was located between 0.002 mm/y and 0.005 mm/y, and only a small amount of corrosion products was observed on the coating surface. The coated samples after salt spray and immersion tests maintained sufficient adhesion (17.07 MPa and 19.25 MPa), and the surface aluminum coating was highly reliable for protection of the steel substrate. In general, the reliability of the coating can be further improved by painting the surface of the thicker Al coating. This provides more ideas for the protection of transmission and transformation equipment.