Preparation and Application of 2D MXene-Based Gas Sensors: A Review

• Published in: Chemosensors Vol. 9; no. 8; p. 225
• Main Authors: Li, Qingting, Li, Yanqiong, Zeng, Wen
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01-08-2021
• Subjects: Ammonia; Carbon; Composite materials; Etching; Fluorine; Functional groups; gas sensitivity mechanism; Gas sensors; Gases; Graphene; Heterojunctions; HF etching; Industrial production; Interlayers; Lamellae; Metal oxides; MXene; MXenes; Nanomaterials; P-n junctions; P-type semiconductors; Polymers; Porosity; Room temperature; Sensitivity; Sensors; Specific surface; Surface area; Two dimensional materials
• ISSN: 2227-9040; 2227-9040
• DOI: 10.3390/chemosensors9080225

Since MXene (a two-dimensional material) was discovered in 2011, it has been favored in all aspects due to its rich surface functional groups, large specific surface area, high conductivity, large porosity, rich organic bonds, and high hydrophilicity. In this paper, the preparation of MXene is introduced first. HF etching was the first etching method for MXene; however, HF is corrosive, resulting in the development of the in situ HF method (fluoride + HCl). Due to the harmful effects of fluorine terminal on the performance of MXene, a fluorine-free preparation method was developed. The increase in interlayer spacing brought about by adding an intercalator can affect MXene’s performance. The usual preparation methods render MXene inevitably agglomerate and the resulting yields are insufficient. Many new preparation methods were researched in order to solve the problems of agglomeration and yield. Secondly, the application of MXene-based materials in gas sensors was discussed. MXene is often regarded as a flexible gas sensor, and the detection of ppb-level acetone at room temperature was observed for the first time. After the formation of composite materials, the increasing interlayer spacing and the specific surface area increased the number of active sites of gas adsorption and the gas sensitivity performance improved. Moreover, this paper discusses the gas-sensing mechanism of MXene. The gas-sensing mechanism of metallic MXene is affected by the expansion of the lamellae and will be doped with H2O and oxygen during the etching process in order to become a p-type semiconductor. A p-n heterojunction and a Schottky barrier forms due to combinations with other semiconductors; thus, the gas sensitivities of composite materials are regulated and controlled by them. Although there are only several reports on the application of MXene materials to gas sensors, MXene and its composite materials are expected to become materials that can effectively detect gases at room temperature, especially for the detection of NH3 and VOC gas. Finally, the challenges and opportunities of MXene as a gas sensor are discussed.