Study of prelocalized graphite/styrene acrylonitrile conducting composites for device applications

• Published in: Physica status solidi. A, Applications and materials science Vol. 203; no. 2; pp. 386 - 396
• Main Authors: Sachdev, V. K., Panwar, Varij, Singh, H., Mehra, N. C., Mehra, R. M.
• Format: Journal Article
• Language: English
• Published: Berlin WILEY-VCH Verlag 01-02-2006; WILEY‐VCH Verlag
• Subjects: 68.37.Hk; 72.80.Tm; 81.05.Qk; 81.20.Ev; 84.37.+q
• ISSN: 1862-6300; 1862-6319
• DOI: 10.1002/pssa.200521101

Conductive polymer composites were prepared by compression molding of prelocalized graphite on to styrene acrylonitrile (SAN) particles. The electrical conductivity is found to be strongly dependent on the graphite content. Three different series were prepared for different processing and material parameters. A low percolation threshold has been noticed when only 1 wt% of graphite is incorporated. Resistivity as low as ∼14 Ω cm has been achieved in a composite with SAN resin particles of 180–212 µm size and graphite 10–20 µm at 90 °C, 105 MPa and 15 min. An electrically conducting network of graphite channels has been observed using scanning electron microscopy. V–I characteristic reveals that at a lower percentage of graphite the increase in current with increase in electric field is due to the hopping/tunneling of electrons, while for higher percentages of graphite ohmic behavior similar to metals has been observed. The data has been analyzed using percolation model. The value of the exponent t that determines the increase in electrical conductivity above the percolation threshold is found to be close to the values given in the literature. The theoretically calculated values of conductivity are found to be in satisfactory agreement with the experimental ones. (© 2006 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)