Durability of self-consolidating concrete to sulfate attack under combined cyclic environments and flexural loading

• Published in: Cement and concrete research Vol. 39; no. 3; pp. 206 - 226
• Main Authors: Bassuoni, M.T., Nehdi, M.L.
• Format: Journal Article
• Language: English
• Published: Kidlington Elsevier Ltd 01-03-2009; Elsevier
• Subjects: Air-entrainment; Applied sciences; Buildings. Public works; C-sulfate attack; Concretes. Mortars. Grouts; Durability of constructions; Durability. Pathology. Repairing. Maintenance; E-composite cements; E-hybrid fibre reinforcement; Exact sciences and technology; Materials; Other special applications (sand concrete, roller compacted concrete, heavy concrete, architectural concrete, etc.); Performance tests; Self-consolidating concrete; Self-consolidating concrete; Performance tests; C-sulfate attack; E-composite cements; Air-entrainment; E-hybrid fibre reinforcement; Performance evaluation; Scanning electron microscopy; Construction materials; Fiber reinforced material; Durability; Experimental study; Sulfates; Self compacting concrete; Composite material; Air entrainment; Chemical attack; Deterioration; Failure analysis; Cement; Dynamic elastic modulus
• ISSN: 0008-8846; 1873-3948
• DOI: 10.1016/j.cemconres.2008.12.003

Classical sulfate immersion tests for concrete have often given different behaviour from that observed in real field exposure. Such tests do not consider other parameters existing in service that can affect the mechanisms and kinetics of sulfate attack. On the other hand, the current shift towards performance-based standards and specifications for concrete requires the development of performance tests that better correlate to field conditions. Such holistic tests can effectively evaluate the service life of normal and emerging types of concrete. With the growing use of self-consolidating concrete (SCC) in various infrastructure applications, it has become necessary to establish reliable data on its durability. In the present study, the durability of a wide range of SCC mixture designs to sulfate attack is assessed when other concomitant damage mechanisms (cyclic environmental conditions and flexural loading) are considered. Based on the tested mixture design variables (type of binders, air-entrainment, sand-to-total aggregates mass ratio, and hybrid fibre reinforcement), potential performance risks (in terms of physico-mechanical parameters) under such a combined exposure were identified. Those risks were not tangible under a full-immersion test method. Thermal, mineralogical and microscopy analyses revealed the coexistence of complex deterioration processes in SCC under the combined exposure, which is fundamentally different from the occurrence of a single damage mechanism (sulfate attack).