Direct dimethyl ether synthesis from syngas on copper–zeolite hybrid catalysts with a wide range of zeolite particle sizes

• Published in: Chinese journal of catalysis Vol. 338; pp. 227 - 238
• Main Authors: Cai, M., Palčić, A., Subramanian, V., Moldovan, S., Ersen, O., Valtchev, V., Ordomsky, V.V., Khodakov, A.Y.
• Format: Journal Article
• Language: English
• Published: San Diego Elsevier Inc 01-06-2016; Elsevier BV; Elsevier
• Subjects: Catalysis; Catalysts; Chemical Sciences; Chemical synthesis; Copper; Crystals; Deactivation; Dimethyl ether synthesis; External surface acidity; Material chemistry; Particle size; ZSM-5; Particle size; Dimethyl ether synthesis; Deactivation; External surface acidity; ZSM-5
• ISSN: 0021-9517; 1872-2067; 1090-2694
• DOI: 10.1016/j.jcat.2016.02.025

[Display omitted]
•Direct DME synthesis from syngas strongly affected by the zeolite particle sizes.•Influence of zeolite particle sizes more significant than the effect of acidity.•Enhanced diffusion of the reaction intermediates with smaller zeolite particles.•Less deactivation with lower concentration of acid sites on the external surface.
This paper reports on direct dimethyl ether synthesis from syngas on hybrid bifunctional copper–zeolite catalysts. Both laboratory synthesized and commercial zeolites were used in this work. The catalyst performance is evaluated under pressure in a continuous fixed bed milli-reactor. The relationships between zeolite particle sizes, acidity and catalytic performance of the hybrid catalysts in dimethyl ether synthesis have been studied. The catalysts and catalyst precursors were characterized using a wide range of characterization techniques: nitrogen adsorption–desorption measurements, X-ray diffraction, 27Al NMR, scanning electron microscopy, transmission electron microscopy and Fourier transform infrared spectroscopy with adsorbed molecular probes.
It is found that the reaction rate in direct dimethyl ether synthesis is strongly affected by the sizes of zeolite particles. The hybrid catalysts containing small individual nanosized zeolite particles (60–100nm) were much active than their counterparts with intergrown crystal agglomerates. The phenomenon is interpreted in terms of enhanced transport of methanol from the copper catalyst to the acid sites in the small zeolite particles with a shift of the thermodynamic equilibrium. The catalyst deactivation was attributed to copper sintering in the presence of the acid sites on the external surface of zeolites. It is established that the catalyst deactivation is less significant with the catalysts containing ZSM-5 zeolites with lower concentration of acid sites on the zeolite external surface. A new methodology to enhance the catalytic performance and stability of copper–zeolite hybrid catalysts for direct dimethyl ether synthesis is proposed.