Silica Bifunctional Supports for the Direct Synthesis of H2O2: Optimization of Br/Acid Sites and Pd/Br Ratio

• Published in: Catalysts Vol. 12; no. 7; p. 796
• Main Authors: Gema Blanco-Brieva, Frederique Desmedt, Pierre Miquel, Jose M. Campos-Martin, Jose L. G. Fierro
• Format: Journal Article
• Language: English
• Published: MDPI AG 01-07-2022
• Subjects: bromide; direct synthesis; hydrogen peroxide; silica bifunctional supports
• ISSN: 2073-4344
• DOI: 10.3390/catal12070796

We have studied the direct synthesis of hydrogen peroxide using a catalytic system consisting of palladium supported on silica bifunctionalized with sulfonic acid groups and bromide in the absence of acid and halide promoters in solution. Catalysts with several bromide substituents were employed in the catalyst synthesis. The prepared samples were characterized by TXRF, XPS, and hydrogen peroxide decomposition. Catalysts characterization indicated the presence of only palladium (II) species in all of the samples, with similar values for surface and bulk of Pd/Br atomic ratio. The catalysts were tested via direct synthesis, and all samples were able to produce hydrogen peroxide at 313 K and 5.0 MPa. The hydrogen peroxide yield and selectivity changed with the Pd/Br ratio. A decrease in the Pd/Br ratio increases the final hydrogen peroxide concentration, and the selectivity for H2O2 reaches a maximum at a Pd/Br ratio around 0.16 and then decreases. However, the maximum hydrogen peroxide concentration and selectivity occur at slightly different Pd/Br ratios, i.e., resp. 0.4 vs. 0.16.