Insecticidal property of Ocimum essential oil embedded polylactic acid packaging films for control of Sitophilus oryzae and Callosobruchus chinensis

• Published in: International journal of biological macromolecules Vol. 256; no. Pt 2; p. 128298
• Main Authors: Prabhakar, Patole Reshma, Reddy, Jeevan Prasad, Keshava Murthy, P.S., Vivek Babu, C.S.
• Format: Journal Article
• Language: English
• Published: Netherlands Elsevier B.V 01-01-2024
• Subjects: Callosobruchus chinensis; Essential oil; Insect proof polymer; Poly lactic acid; Sitophilus oryzae; Poly lactic acid; Essential oil; Insect proof polymer; Sitophilus oryzae; Callosobruchus chinensis
• ISSN: 0141-8130; 1879-0003
• DOI: 10.1016/j.ijbiomac.2023.128298

Naturally derived essential oils (EOs) from Ocimum basilicum (OB) and Ocimum gratissimum (OG) were incorporated in polylactic acid (PLA) matrix with concentration of 2.5 % and 5 % respectively by solvent casting method, with an aim to develop insecticidal polymer pouches (insect proof polymer pouches). The major components following GC–MS analysis revealed the presence of EOs as estragole (69.998 %) in OB and thymol (29.843 %) in OG. The developed films with EOs showed remarkable insecticidal activity with 100 % and 80 % mortality rate for OB and OG respectively at 2.5 % concentration against rice weevil (Sitophilus oryzae). While, both OB and OG EOs observed 100 % mortality against pulse beetle (Callosobruchus chinensis) after 96 h exposure in presence of grain conditions and the insecticidal efficacy was equivalent to the commercial hermetic bags (CSB). The physical property of film showed increase in the film thickness in EO-PLA films whereas the mechanical properties of EO-PLA films matrix have increased the polymer flexibility with decreasing tensile strength (TS) and Youngs modulus (EM) as TS OB 5 %, OG 5 % - 15.64 MPa, 17.66 MPa respectively. While, water vapour transmission rate (WVTR) was reduced to 0.015 g/m2.hr, optical characteristics showed slight significant change in colour and FTIR spectra exhibited a change in -OH stretching compared to blank PLA matrix. The surface morphology of the blank and EO embedded PLA films visualized by SEM depicted a complete homogenization of essential oils in the PLA matrix.