3D printing of cordierite materials from raw reactive mixtures

• Published in: Ceramics international Vol. 49; no. 3; pp. 4578 - 4585
• Main Authors: Dorado, B., Moreno-Sanabria, L., García, E., Belmonte, M., Miranzo, P., Osendi, M.I.
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 01-02-2023
• Subjects: 3D printing; Compression strength; Cordierite; Ink rheology; Thermal conductivity; Thermal expansion coefficient; Thermal expansion coefficient; Cordierite; Thermal conductivity; Ink rheology; 3D printing; Compression strength
• ISSN: 0272-8842; 1873-3956
• DOI: 10.1016/j.ceramint.2022.09.343

Porous cordierite materials are 3D printed by robocasting from two kaolin containing raw materials mixtures. Water suspensions of both mixtures at variable solid concentrations (40–67 wt%) are characterized by rheological measurements, showing good printability for concentrations >60 wt% without the need of any printing additive. The mixtures react during sintering (at 1250 °C) giving indialite as the main phase in the structures, which differ in minor phases. Three types of lattices are printed for both compositions with a logpile inner structure. Properties of interest like the coefficient of thermal expansion (CTE), the thermal conductivity (KT) and the compression strength (σ) of the printed cordierites are determined and compared with published data. Results evidence that printing of clay containing reactive mixtures is a straightforward and cost-effective way to achieve porous complex shaped cordierite with CTE∼ 2–3 x10−6 K-1, KT ∼ 0.4–0.6 W m−1 K−1 and maximum σ of 24 MPa.