Application of Calcium Silicate Materials After Acid Etching May Preserve Resin-Dentin Bonds

• Published in: Operative dentistry Vol. 43; no. 5; pp. E243 - E252
• Main Authors: Aggarwal, V, Bhasin, S S
• Format: Journal Article
• Language: English
• Published: United States 01-09-2018
• Subjects: Acid Etching, Dental - methods; Calcium Compounds - therapeutic use; Dental Bonding - methods; Dental Marginal Adaptation; Dental Restoration, Permanent - methods; Dentin - metabolism; Dentistry; Humans; Microscopy, Electron, Scanning; Molar - surgery; Resins, Synthetic - therapeutic use; Silicates - therapeutic use
• ISSN: 0361-7734; 1559-2863
• DOI: 10.2341/17-306-l

The aim of the present study was to evaluate the effect of the application of calcium silicate materials (CSMs), after acid etching, on the longevity of the hybrid layer and marginal adaptation of composite restorations.
Eighty human permanent molars received an intrapulpal pressure of 15 cm H
O. Sixty teeth received a mesial proximal slot preparation with the gingival margin extending 1 mm below the cemento-enamel junction. The samples were divided into two groups. Group 1 received restorations using two types of etch-and-rinse adhesives: ethanol based (Single Bond, 3M ESPE, St Paul, MN, USA) and acetone based (Prime & Bond NT, Dentsply, DeTrey GmbH, Germany). In group 2 samples, a commercially available CSM (ProRoot MTA) was allowed to set before grinding and placing into a distilled water solution. This solution was applied on the cavity floor after acid etching. The surface was washed after 30 seconds followed by application of adhesives and restorations as in group 1. The samples were stored in phosphate-buffered saline for six months, maintaining the intrapulpal pressure. An epoxy replica was made, and the marginal adaptation was evaluated using scanning electron microscopy. The percentage of continuous margin (CM) was recorded for each group. Another 20 samples were used for hybrid layer evaluation. The crowns were ground to expose dentin. Intrapulpal pressure was applied. The samples were divided into two groups and restored similar to samples restored for marginal adaptation evaluation. The samples were longitudinally cut in 1-mm slices. The slices were stored under 15 cm of phosphate-buffered saline to simulate the pulpal pressure. After six months, the adhesive interface was evaluated using a scanning electron microscope. Statistical analysis was done with two-way analysis of variance with Holm-Sidak's correction for multiple comparisons.
Application of CSMs improved the marginal adaptation values in both adhesive groups. In group 1, there were areas of incomplete penetration of resins along with evidence of partial degradation of resin tags. Samples receiving CSM application after acid etching demonstrated long and regular resin tags with very few signs of degradation.
Application of CSMs after acid etching can be a potential avenue in preserving the resin-dentin bonds.