Effective corrosion protection of AA6061 aluminum alloy by sputtered Al–Ce coatings

• Published in: Electrochimica acta Vol. 55; no. 2; pp. 498 - 503
• Main Authors: Domínguez-Crespo, M.A., Torres-Huerta, A.M., Rodil, S.E., Ramírez-Meneses, E., Suárez-Velázquez, G.G., Hernández-Pérez, M.A.
• Format: Journal Article
• Language: English
• Published: Kidlington Elsevier Ltd 30-12-2009; Elsevier
• Subjects: AA6061; Al–Ce films; Applied sciences; Coatings; Corrosion; Corrosion prevention; Corrosion properties; Exact sciences and technology; Magnetron sputtering; Metals. Metallurgy; Magnetron sputtering; Coatings; Corrosion properties; AA6061; Al–Ce films; Atomic force microscopy; Scanning electron microscopy; Aluminium base alloys; Coating material; Cerium alloy; Corrosion inhibition; Corrosion protection; X ray diffraction; Surface structure; Tafel curve; Al-Ce films; Metal coating; Transmission electron microscopy; Morphology; Physical vapor deposition; Kinetics; Binary alloy; Electrochemical impedance spectroscopy
• ISSN: 0013-4686; 1873-3859
• DOI: 10.1016/j.electacta.2009.09.002

Al–Ce coatings were deposited on silicon and AA6061 aluminum alloy substrates by DC magnetron sputtering using aluminum in combination with pure cerium targets. The materials were characterized by X-ray diffraction (XRD), atomic force microscopy (AFM), scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM) and electrochemical impedance spectroscopy (EIS) in order to consider their application as high corrosion resistance coatings. The corrosion behavior of the films was studied using a NaCl aqueous solution (3.5
wt%). As for the characterization results, an apparent amorphous phase of aluminum oxide with small cerium compounds embedded in the matrix was detected by the X-ray diffraction patterns and HRTEM on the deposited films at 200
W and 4
Pa. At these conditions, AFM and SEM images evidenced crack-free coatings with low-roughness nanometric structures and columnar growth. EIS and Tafel results converged to indicate an inhibition of the corrosion reactions. The film displayed good stability in the aggressive medium and after 1 day of exposure underwent very little degradation. The variations in the impedance and Tafel characteristics were found to occur as a function of cerium content, which provokes important changes in the film protective properties.