Characterization of AlGaN-based metal–semiconductor solar-blind UV photodiodes with IrO2 Schottky contacts

• Published in: Physica. B, Condensed matter Vol. 407; no. 10; pp. 1529 - 1532
• Main Authors: van Schalkwyk, L., Meyer, W.E., Auret, F.D., Nel, J.M., Ngoepe, P.N.M., Diale, M.
• Format: Journal Article Conference Proceeding
• Language: English
• Published: Kidlington Elsevier B.V 15-05-2012; Elsevier
• Subjects: AlGaN; Annealing; Applied sciences; Barriers; Condensed matter; Current density; Density; Electronics; Exact sciences and technology; Gold; Iridium; Iridium oxide; Optoelectronic; Optoelectronic devices; Photodiode; Photodiodes; Schottky; Semiconductor electronics. Microelectronics. Optoelectronics. Solid state devices; Solar-blind; Ultraviolet; Schottky; Iridium oxide; Optoelectronic; Photodiode; Ultraviolet; AlGaN; Solar-blind; Annealing; Semiconductor materials; Voltage current curve; Fluence; Ultraviolet radiation; Ultraviolet detector; Ion irradiation; Aluminium Gallium Nitrides Mixed; Leakage current; Barrier height; Series resistance; Schottky barrier; Voltage capacity curve
• ISSN: 0921-4526; 1873-2135
• DOI: 10.1016/j.physb.2011.09.078

Intrinsically solar-blind ultraviolet (UV) AlGaN-based Schottky photodiodes were fabricated using Iridium oxide (IrO2) as the Schottky barrier material. The Ir Schottky contacts were annealed at 700°C under O2 ambient and the photodiodes characterized with an optoelectronic system. The main parameters extracted from I–V measurements were an average ideality factor of 1.38, a Schottky barrier height of 1.52eV, a reverse leakage current density at −1V bias of 5.2nA/cm2 and series resistance of 250Ω. After spectral characterization, it was found that annealing, alone, of the Ir contact to form the more UV transmissive IrO2 does not always improve the responsivity. The deposition of a Au probe contact on the IrO2 contact increased the responsivity from 40mA/W to 52mA/W at 275nm with respect to the annealed Ir contact. However, the ideality factor degraded to 1.57, Schottky barrier height lowered to 1.19eV, reverse leakage current density increased to 49nA/cm2 and series resistance decreased to 100Ω with the addition of the Au contact. The radiation hardness of AlGaN was also confirmed after studying the effects of 5.4MeV He-ion irradiation using 241Am for a total fluence of 3×1013cm−2.