Viscoelastic properties of the equine hoof wall

• Published in: Acta biomaterialia Vol. 184; pp. 264 - 272
• Main Authors: Bonney, Christian, Pang, Siyuan, Meyers, Marc A., Jasiuk, Iwona
• Format: Journal Article
• Language: English
• Published: England Elsevier Ltd 01-08-2024
• Subjects: Animals; Biological material; Dynamic mechanical analysis; Elastic Modulus; Elasticity; Hoof and Claw - physiology; Hoof wall; Horses - anatomy & histology; Impact resistance; Nanoindentation; Viscoelasticity; Viscosity; Viscoelasticity; Impact resistance; Hoof wall; Dynamic mechanical analysis; Biological material; Nanoindentation
• ISSN: 1742-7061; 1878-7568; 1878-7568
• DOI: 10.1016/j.actbio.2024.06.022

The equine hoof wall has outstanding impact resistance, which enables high-velocity gallop over hard terrain with minimum damage. To better understand its viscoelastic behavior, complex moduli were determined using two complementary techniques: conventional (∼5 mm length scale) and nano (∼1 µm length scale) dynamic mechanical analysis (DMA). The evolution of their magnitudes was measured for two hydration conditions: fully hydrated and ambient. The storage modulus of the ambient hoof wall was approximately 400 MPa in macro-scale experiments, decreasing to ∼250 MPa with hydration. In contrast, the loss tangent decreased for both hydrated (∼0.1–0.07) and ambient (∼0.04–0.01) conditions, over the frequency range of 1–10 Hz. Nano-DMA indentation tests conducted up to 200 Hz showed little frequency dependence beyond 10 Hz. The loss tangent of tubular regions showed more hydration sensitivity than in intertubular regions, but no significant difference in storage modulus was observed. Loss tangent and effective stiffness were higher in indentations for both hydration levels. This behavior is attributed to the hoof wall's hierarchical structure, which has porosity, functionally graded aspects, and material interfaces that are not captured at the scale of indentation. The hoof wall's viscoelasticity characterized in this work has implications for the design of bioinspired impact-resistant materials and structures.
The outer wall of horse hooves evolved to withstand heavy impacts during gallop. While previous studies have measured the properties of the hoof wall in slowly changing conditions, we wanted to quantify its behavior using experiments that replicate the quickly changing forces of impact. Since the hoof wall's structure is complex and contributes to its overall performance, smaller scale experiments were also performed. The behavior of the hoof wall was within the range of other biological materials and polymers. When hydrated, it becomes softer and can dissipate more energy. This work improves our understanding of the hoof's function and allows for more accurate simulations that can account for different impact speeds.