Switchable Catalysis Improves the Properties of CO 2 -Derived Polymers: Poly(cyclohexene carbonate- b -ε-decalactone- b -cyclohexene carbonate) Adhesives, Elastomers, and Toughened Plastics

• Published in: Journal of the American Chemical Society Vol. 142; no. 9; pp. 4367 - 4378
• Main Authors: Sulley, Gregory S, Gregory, Georgina L, Chen, Thomas T D, Peña Carrodeguas, Leticia, Trott, Gemma, Santmarti, Alba, Lee, Koon-Yang, Terrill, Nicholas J, Williams, Charlotte K
• Format: Journal Article
• Language: English
• Published: United States 04-03-2020
• ISSN: 0002-7863; 1520-5126
• DOI: 10.1021/jacs.9b13106

Carbon dioxide/epoxide copolymerization is an efficient way to add value to waste CO
and to reduce pollution in polymer manufacturing. Using this process to make low molar mass polycarbonate polyols is a commercially relevant route to new thermosets and polyurethanes. In contrast, high molar mass polycarbonates, produced from CO
, generally under-deliver in terms of properties, and one of the most widely investigated, poly(cyclohexene carbonate), is limited by its low elongation at break and high brittleness. Here, a new catalytic polymerization process is reported that selectively and efficiently yields degradable ABA-block polymers, incorporating 6-23 wt % CO
. The polymers are synthesized using a new, highly active organometallic heterodinuclear Zn(II)/Mg(II) catalyst applied in a one-pot procedure together with biobased ε-decalactone, cyclohexene oxide, and carbon dioxide to make a series of poly(cyclohexene carbonate-
-decalactone-
-cyclohexene carbonate) [PCHC-PDL-PCHC]. The process is highly selective (CO
selectivity >99% of theoretical value), allows for high monomer conversions (>90%), and yields polymers with predictable compositions, molar mass (from 38-71 kg mol
), and forms dihydroxyl telechelic chains. These new materials improve upon the properties of poly(cyclohexene carbonate) and, specifically, they show good thermal stability (
∼ 280 °C), high toughness (112 MJ m
), and very high elongation at break (>900%). Materials properties are improved by precisely controlling both the quantity and location of carbon dioxide in the polymer chain. Preliminary studies show that polymers are stable in aqueous environments at room temperature over months, but they are rapidly degraded upon gentle heating in an acidic environment (60 °C, toluene,
-toluene sulfonic acid). The process is likely generally applicable to many other lactones, lactides, anhydrides, epoxides, and heterocumulenes and sets the scene for a host of new applications for CO
-derived polymers.