HOT CORROSION OF CERIA-YTTRIA STABILIZED ZIRCONIA PLASMA SPRAYED THERMAL BARRIER COATING BY EUTECTIC VANDIUM PENTAOXIDE-SODIUM SULFATE

• Published in: The Iraqi journal for mechanical and materials engineering. Vol. 18; no. 1; pp. 182 - 192
• Main Authors: Kadhim, Mohammed J, Hafiz, Mohammed H, Ali Bash, Maryam A
• Format: Journal Article
• Language: English
• Published: 31-07-2018
• ISSN: 1819-2076; 2313-3783
• DOI: 10.32852/iqjfmme.Vol18.Iss1.83

The high temperature corrosion behavior of thermal barrier coating (TBC) systemconsisting of IN-738 LC superalloy substrate, air plasma sprayed Ni24.5Cr6Al0.4Y (wt%)bond coat and air plasma sprayed ZrO2-20 wt% ceria-3.6 wt% yttria (CYSZ) ceramic coatwere characterized. The upper surfaces of CYSZ covered with 30 mg/cm2 , mixed 45 wt%Na2SO4-55 wt% V2O5 salt were exposed at different temperatures from 800 to 1000 oC andinteraction times from 1 up to 8 h. The upper surface plan view of the coatings wereidentified for topography, roughness, chemical composition, phases and reaction productsusing scanning electron microscopy, energy dispersive spectroscopy, talysurf, and X-raydiffraction. XRD analyses of the plasma sprayed coatings after hot corrosion confirmed thephase transformation of nontransformable tetragonal (t') into monoclinic phase, presence ofYVO4 and CeVO4 products. Analysis of the hot corrosion CYSZ coating confirmed theformation of high volume fraction of YVO4, with low volume fractions of CeOV4 and CeO2.The formation of these compounds were combined with formation of monoclinic phase (m)from transformation of nontransformable tetragonal phase (t').