In-Capillary Photodeposition of Glyphosate-Containing Polyacrylamide Nanometer-Thick Films

• Published in: ACS applied polymer materials Vol. 5; no. 1; pp. 223 - 235
• Main Authors: Mazuryk, Jaroslaw, Klepacka, Katarzyna, Piechowska, Joanna, Kalecki, Jakub, Derzsi, Ladislav, Piotrowski, Piotr, Paszke, Piotr, Pawlak, Dorota A., Berneschi, Simone, Kutner, Wlodzimierz, Sharma, Piyush Sindhu
• Format: Journal Article
• Language: English
• Published: United States American Chemical Society 13-01-2023
• Subjects: photopolymerization; silanization; fused silica microcapillary; nanofilm; confocal micro-Raman spectroscopy; microfluidics; polyacrylamide; glyphosate
• ISSN: 2637-6105; 2637-6105
• DOI: 10.1021/acsapm.2c01461

The present research reports on in-water, site-specific photodeposition of glyphosate (GLP)-containing polyacrylamide (PAA-GLP) nanometer-thick films (nanofilms) on an inner surface of fused silica (fused quartz) microcapillaries presilanized with trimethoxy­(octen-7-yl)­silane (TMOS). TMOS was chosen because of the vinyl group presence in its structure, enabling its participation in the (UV light)-activated free-radical polymerization (UV-FRP) after its immobilization on a fused silica surface. The photodeposition was conducted in an aqueous (H2O/ACN; 3:1, v/v) solution, using UV-FRP (λ = 365 nm) of the acrylamide (AA) functional monomer, the N,N′-methylenebis­(acrylamide) (BAA) cross-linking monomer, GLP, and the azobisisobutyronitrile (AIBN) UV-FRP initiator. Acetonitrile (ACN) was used as the porogen and the solvent to dissolve monomers and GLP. Because of the micrometric diameters of microcapillaries, the silanization and photodeposition procedures were first optimized on fused silica slides. The introduction of TMOS, as well as the formation of PAA and PAA-GLP nanofilms, was determined using atomic force microscopy (AFM), scanning electron microscopy with energy-dispersive X-ray (SEM–EDX) spectroscopy, and confocal micro-Raman spectroscopy. Particularly, AFM and SEM–EDX measurements determined nanofilms’ thickness and GLP content, respectively, whereas in-depth confocal (micro-Raman spectroscopy)-assisted imaging of PAA- and PAA-GLP-coated microcapillary inner surfaces confirmed the successful photodeposition. Moreover, we examined the GLP impact on polymer gelation by monitoring hydration in a hydrogel and a dried powder PAA-GLP. Our study demonstrated the usefulness of the in-capillary micro-Raman spectroscopy imaging and in-depth profiling of GLP-encapsulated PAA nanofilms. In the future, our simple and inexpensive procedure will enable the fabrication of polymer-based microfluidic chemosensors or adsorptive-separating devices for GLP detection, determination, and degradation.