Large-Diameter Single-Wall Carbon Nanotubes Formed Alongside Small-Diameter Double-Walled Carbon Nanotubes

• Published in: Journal of physical chemistry. C Vol. 119; no. 3; pp. 1524 - 1535
• Main Authors: Kasperski, Anne, Weibel, Alicia, Datas, Lucien, De Grave, Eddy, Peigney, Alain, Laurent, Christophe
• Format: Journal Article
• Language: English
• Published: American Chemical Society 22-01-2015
• Subjects: Chemical Sciences; Organic chemistry; Formed Alongside; Single-Wall Carbon Nanotubes; Double-Walled Carbon Nanotubes; Large-Diameter; Small-Diameter
• ISSN: 1932-7447; 1932-7455
• DOI: 10.1021/jp509080e

Samples containing a majority of either single-wall carbon nanotubes (SWCNTs) or double-walled carbon nanotubes (DWCNTs) are prepared in the same catalytic chemical vapor deposition conditions but using slightly different catalytic materials, based on alumina impregnated with iron and molybdenum salts. There is a sharp SWCNTs-to-DWCNTs transition. By contrast to the usual findings, the selectivity is not correlated to the size of the iron-based catalyst nanoparticles, nor does the transition occur upon a decreasing carbon/catalyst ratio. The result is attributed to the increasing MoO3 concentration inducing modifications of the gas atmosphere, such as the formation of more reactive C2 species through C2H4 dissociation, which thus favors the nucleation and growth of a DWCNT. In the DWCNT sample, the average diameter of the SWCNTs is higher than the average outer diameter of the DWCNTs, which is uncommon, as many authors stress that SWCNTs show a lower diameter than DWCNTs. The study could provide guidelines for the synthesis of very small diameter DWCNTs.