Effects of Peracetic Acid on the Corrosion Resistance of Commercially Pure Titanium (grade 4)

• Published in: Brazilian dental journal Vol. 26; no. 6; p. 660
• Main Authors: Raimundo, Lariça B, Orsi, Iara A, Kuri, Sebastião E, Rovere, Carlos Alberto D, Busquim, Thaís P, Borie, Eduardo
• Format: Journal Article
• Language: English
• Published: Brazil 01-11-2015
• Subjects: Corrosion; Microscopy, Electron, Scanning; Peracetic Acid - chemistry; Spectrometry, X-Ray Emission; Titanium - chemistry
• ISSN: 1806-4760

The aim of this study was to evaluate the corrosion resistance of pure titanium grade 4 (cp-Ti-4), subjected to disinfection with 0.2% and 2% peracetic acid during different immersion periods using anodic potentiodynamic polarization test in acid and neutral artificial saliva. Cylindrical samples of cp-Ti-4 (5 mm x 5 mm) were used to fabricate 24 working electrodes, which were mechanically polished and divided into eight groups (n=3) for disinfection in 2% and 0.2% peracetic acid for 30 and 120 min. After disinfection, anodic polarization was performed in artificial saliva with pH 4.8 and 6.8 to assess the electrochemical behavior of the electrodes. A conventional electrochemical cell, constituting a reference electrode, a platinum counter electrode, and the working electrode (cp-Ti specimens) were used with a scanning rate of 1 mV/s. Three curves were obtained for each working electrode, and corrosion was characterized by using scanning electron microscopy (SEM) and energy dispersive x-ray spectrometry (EDS). Data of corrosion potential (Ecorr) and passive current (Ipass) obtained by the polarization curves were analyzed statistically by Student's t-test (a=0.05). The statistical analysis showed no significant differences (p>0.05) between artificial saliva types at different concentrations and periods of disinfection, as well as between control and experimental groups. No surface changes were observed in all groups evaluated. In conclusion, disinfection with 0.2% and 2% peracetic acid concentrations did not cause corrosion in samples manufactured with cp-Ti-4.