Phase equilibria in the La–Mg–Ge system at 500 °C and crystal structure of the new ternary compounds La{sub 11}Mg{sub 2}Ge{sub 7} and LaMg{sub 3−x}Ge{sub 2}

• Published in: Journal of solid state chemistry Vol. 218
• Main Authors: De Negri, S., Solokha, P., Skrobańska, M., Proserpio, D.M., Samara Center for Theoretical Materials Science, Saccone, A.
• Format: Journal Article
• Language: English
• Published: United States 15-10-2014
• Subjects: CUBIC LATTICES; GERMANIDES; INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; MONOCLINIC LATTICES; MONOCRYSTALS; ORTHORHOMBIC LATTICES; PHASE DIAGRAMS; TETRAGONAL LATTICES; X RADIATION; X-RAY DIFFRACTION
• ISSN: 0022-4596; 1095-726X
• DOI: 10.1016/J.JSSC.2014.06.036

The whole 500 °C isothermal section of the La–Mg–Ge ternary system was constructed. The existence and crystal structure of three ternary compounds were confirmed: La{sub 2+x}Mg{sub 1−x}Ge{sub 2} (τ{sub 2}, P4/mbm, tP10–Mo{sub 2}FeB{sub 2}, 0≤x≤0.25), La{sub 4}Mg{sub 5}Ge{sub 6} (τ{sub 3}, Cmc2{sub 1}, oS60–Gd{sub 4}Zn{sub 5}Ge{sub 6}) and La{sub 4}Mg{sub 7}Ge{sub 6} (τ{sub 4}, C2/m, mS34, own structure type). Five novel compounds were identified and structurally characterized: La{sub 11}Mg{sub 2}Ge{sub 7} (τ{sub 1}, P4{sub 2}/ncm, tP88-8, own structure type, a=1.21338(5), c=1.57802(6) nm), LaMg{sub 3−x}Ge{sub 2} (τ{sub 5}, P3{sup ¯}1c, hP34-0.44, own structure type, x=0.407(5), a=0.78408(4), c=1.45257(7) nm), La{sub 6}Mg{sub 23}Ge (τ{sub 6}, Fm3{sup ¯}m, cF120–Zr{sub 6}Zn{sub 23}Si, a=1.46694(6) nm), La{sub 4}MgGe{sub 10−x} (τ{sub 7}, x=0.37(1), C2/m, mS60-1.46, own structure type, a=0.88403(8), b=0.86756(8), c=1.7709(2) nm, β=97.16°(1) and La{sub 2}MgGe{sub 6} (τ{sub 8}, Cmce, oS72–Ce{sub 2}(Ga{sub 0.1}Ge{sub 0.9}){sub 7}, a=0.8989(2), b=0.8517(2), c=2.1064(3) nm). Disordering phenomena were revealed in several La–Mg–Ge phases in terms of partially occupied sites. The crystal structures of La{sub 11}Mg{sub 2}Ge{sub 7} and LaMg{sub 3−x}Ge{sub 2} are discussed in details. The latter is a √3a×√3a×2c superstructure of the LaLi{sub 3}Sb{sub 2} structure type; the symmetry reduction scheme is shown in the Bärnighausen formalism terms. - Graphical abstract: La–Mg–Ge isothermal section at 500 °C and group–subgroup relation between the LaLi{sub 3}Sb{sub 2} (parent type) and LaMg{sub 3−x}Ge{sub 2} (derivative) structures. - Highlights: • Novel La−Mg−Ge compounds structure determination from X-ray single crystal data. • Disordering phenomena as common features of the studied germanides. • Bärnighausen formalism as a useful tool for accurate structure determination. • Full isothermal section of the La–Mg–Ge ternary system at 500 °C.