Effect of pH of H2O2 solutions on the morphology and wear resistance of human dental enamel: an AFM study

• Published in: Annals of medicine (Helsinki) Vol. 53; no. S1; p. S52
• Main Authors: Branco, A. C., Polido, M., Colaço, R., Figueiredo-Pina, C. G., Serro, A. P.
• Format: Journal Article
• Language: English
• Published: Taylor & Francis 01-04-2021; Taylor & Francis Group
• Subjects: Abstract; Abstract 104
• ISSN: 0785-3890; 1365-2060
• DOI: 10.1080/07853890.2021.1897311

Teeth whitening is a highly demanded aesthetic dental procedure to remove teeth stains and get a whiter and perfect smile. This type of treatment is usually performed by the application on the teeth surface of hydrogen or carbamide peroxides which diffuse through the external layer of the teeth, enamel [
1
]. Although whitening treatments improve teeth appearance, they can impair teeth health, due to the eventual degradation of the teeth tissues. This may lead to abnormal wear and weaken the tooth structure. The aim of this work is to study the effect of the pH of 30% H
2
O
2
solutions on the surface of human enamel.
Human molars were collected for the study with informed consents of the patients. Teeth were bleached in 30% H
2
O
2
solution with different pH values (2, 4 and 6). All samples were submitted to 11 bleaching sessions of 10 min each with alternate periods (2 min) of exposition to blue light. Microhardness, surface roughness and topography/morphology were characterised by microindentation tests, atomic force microscopy (AFM) and scanning electron microscopy (SEM), respectively, before and after the whitening treatments. AFM scratching tests (10 × 10 µm
2
) were performed, using a diamond probe. After the nanowear tests, topographical images of larger areas (20 × 20 µm
2
) which include the scratched squares were obtained with a silicon probe. The wear mechanisms were evaluated by SEM. Acceptance of the study protocol was obtained from a local ethics committee.
The most significant changes on enamel surface were obtained for pH = 2: the microhardness decreases, and the surface roughness significantly increases as confirmed by the SEM image analysis. A higher wear rate was observed for pH = 2 in the AFM scratching tests. SEM observation of the wear zone showed differences in the wear mechanisms, which depend on the pH.
Enamel microhardness, surface roughness and wear resistance are affected by the pH of the bleaching solution: pH = 2 led to the most adverse effects, which was attributed to hydroxyapatite demineralisation. The study of the effect of pH in the bleaching treatments is crucial to optimise this type of procedures and avoids enamel damage.