Comparative evaluation of shear bond strength and microleakage of tricalcium silicate-based restorative material and radioopaque posterior glass ionomer restorative cement in primary and permanent teeth: An in vitro study

• Published in: Journal of the Indian Society of Pedodontics and Preventive Dentistry Vol. 32; no. 4; pp. 304 - 310
• Main Authors: Raju, Vignesh, Venumbaka, Nilaya, Mungara, Jayanthi, Vijayakumar, Poornima, Rajendran, Sakthivel, Elangovan, Arun
• Format: Journal Article
• Language: English
• Published: Chandigarh Medknow Publications 01-10-2014; Medknow Publications and Media Pvt. Ltd; Medknow Publications & Media Pvt. Ltd; Wolters Kluwer Medknow Publications
• Subjects: Analysis; Aqueous solutions; Biodentine; Bond strength; Cement; Dental caries; Dental equipment and supplies industry; Dentin; Dentistry; glass ionomer cements; Mechanical properties; microleakage; shear bond strength; Silicates; Teeth; Japan; glass ionomer cements; Biodentine; shear bond strength; microleakage
• ISSN: 0970-4388; 1998-3905
• DOI: 10.4103/0970-4388.140952

Background: Restoration of carious primary molars is still a major concern while treating the young children that too in deep carious lesion which extends below the cemento-enamel junction (CEJ) where pulp protection and achieving adequate marginal seal are very important to prevent secondary caries. The needs were met with the development of new materials. One such of new bioactive material is tricalcium silicate-based restorative material (Biodentine), recommended for restoring deep lesions. Aim: To evaluate and compare shear bond strength and microleakage of tricalcium silicate-based restorative material (Biodentine) and glass ionomer cement (Fuji IX GP) in primary and permanent teeth. Materials and Methods: Occlusal surface of crowns were ground flat. PVC molds were stabilized over flat dentin surface and filled with tricalcium silicate-based restorative material (Biodentine)/glass ionomer cement (Fuji IX GP) according to group ascertained. Shear bond strength was evaluated using universal testing machine (INSTRON). Standardized Class II cavities were prepared on both primary and permanent teeth, and then restored with tricalcium silicate-based restorative material (Biodentine)/glass ionomer cement (Fuji IX GP) according to group ascertained, over which composite resin material was restored using an open sandwich technique. Microleakage was assessed using dye penetration. Microleakage was examined using a stereomicroscope. Results: Results showed that glass ionomer cement (Fuji IX GP) exhibited better shear bond strength than tricalcium silicate-based restorative material (Biodentine). Mean microleakage score for glass ionomer cement (Fuji IX GP) in permanent teeth was 1.52 and for primary teeth was 1.56. The mean microleakage for tricalcium silicate-based restorative material (Biodentine) in permanent teeth was 0.76 and for primary teeth was 0.60. Glass ionomer cement (Fuji IX GP) exhibited more microleakage than tricalcium silicate-based restorative material (Biodentine), which was statistically significant both in permanent (P = 0.02) and primary (P = 0.006) teeth. Conclusion: Shear bond strength of glass ionomer cement (Fuji IX GP) is greater than tricalcium silicate-based restorative material (Biodentine) in both primary and permanent teeth. Tricalcium silicate-based restorative material (Biodentine) exhibited less microleakage compared to glass ionomer cement (Fuji IX GP) in both primary and permanent molars.