Formation of metallic Si and SiC nanoparticles from SiO2 particles by plasma-induced cathodic discharge electrolysis in chloride melt

• Published in: Electrochimica acta Vol. 100; pp. 300 - 303
• Main Authors: Tokushige, M., Tsujimura, H., Nishikiori, T., Ito, Y.
• Format: Journal Article
• Language: English
• Published: Elsevier Ltd 30-06-2013
• Subjects: Current efficiency; Direct reduction; Discharge; Electrolysis; Melts; Molten salt; Nanoparticles; Oxide particle; Plasma-induced electrolysis; Silicon; Silicon carbide; Silicon dioxide; Suspension electrolysis; Suspension electrolysis; Direct reduction; Plasma-induced electrolysis; Oxide particle; Molten salt
• ISSN: 0013-4686; 1873-3859
• DOI: 10.1016/j.electacta.2012.08.068

Silicon nanoparticles are formed from SiO2 particles by conducting plasma-induced cathodic discharge electrolysis. In a LiCl–KCl melt in which SiO2 particles were suspended at 450°C, we obtained Si nanoparticles with diameters around 20nm. During the electrolysis period, SiO2 particles are directly reduced by discharge electrons on the surface of the melt just under the discharge, and the deposited Si atom clusters form Si nanoparticles, which leave the surface of the original SiO2 particle due to free spaces caused by a molar volume difference between SiO2 and Si. We also found that SiC nanoparticles can be obtained using carbon anode. Based on Faraday's law, the current efficiency for the formation of Si nanoparticles is 70%.