Microstructural Evolution and Mechanical Behavior of an Al-6061 Alloy Processed by Repetitive Corrugation and Straightening

• Published in: Metals (Basel ) Vol. 10; no. 4; p. 489
• Main Authors: Elizalde, Sergio, Ezequiel, Marco, Figueroa, Ignacio A., Cabrera, José M., Braham, Chedly, Gonzalez, Gonzalo
• Format: Journal Article
• Language: English
• Published: Basel MDPI AG 01-04-2020
• Subjects: Al-alloy; Alloys; Aluminum base alloys; Corrugation; Ductility; Electron backscatter diffraction; Evolution; finite element analysis; Finite element method; Grain size distribution; Hardness; Mechanical properties; Metal sheets; Microstructure; Plastic deformation; Precipitation hardening; RCS; Simulation; Straightening; Stress concentration; Tensile tests; Ultimate tensile strength; Ultrafines; Yield strength; Japan
• ISSN: 2075-4701; 2075-4701
• DOI: 10.3390/met10040489

The repetitive corrugation and straightening process is a severe plastic deformation technique that is particularly suited to process metallic sheets. With this technique, it is possible to develop nano/ultrafine-grained structured materials, and therefore, to improve some mechanical properties such as the yield strength, ultimate tensile strength, and fatigue lifetime. In this study, an Al-6061 alloy was subjected to the repetitive corrugation and straightening process. A new corrugation die design was proposed in order to promote a heterogeneous deformation into the metallic sheet. The evolution of the mechanical properties and microstructure obtained by electron backscatter diffraction of the alloy showed a heterogeneous distribution in the grain size at the initial cycles of the repetitive corrugation and straightening process. Uniaxial tensile tests showed a significant increase in yield strength as the number of repetitive corrugation and straightening passes increased. The distribution of the plastic deformation was correlated with the hardness distribution on the surface. The hardness distribution map matched well with the heterogeneous distribution of the plastic deformation obtained by finite element simulation. A maximum average hardness (147 HV) and yield strength (385 MPa) was obtained for two repetitive corrugation and straightening cycles sample.