High-order nonlinear optical response of a polymer nanocomposite film incorporating semiconducotor CdSe quantum dots

• Published in: Optics express Vol. 20; no. 12; pp. 13457 - 13469
• Main Authors: Liu, Xiangming, Adachi, Yusuke, Tomita, Yasuo, Oshima, Juro, Nakashima, Takuya, Kawai, Tsuyoshi
• Format: Journal Article
• Language: English
• Published: United States 04-06-2012
• ISSN: 1094-4087; 1094-4087
• DOI: 10.1364/oe.20.013457

We report on observation of high-order optical nonlinearities in our recently developed photopolymerizable semiconductor CdSe quantum dot (QD)-polymer nanocomposite films at various volume fractions of CdSe QDs as high as 0.91 vol.% (3.6 wt.%). We performed Z-scan and degenerate multi-wave mixing (DMWM) measurements using a 532-nm picosecond laser delivering single 35 ps pulses at a repetition rate of 10 Hz. Using the uniformly cured polymer nanocomposite films, we observed the third- and fifth-order nonlinear optical effects in closed-aperture Z-scan measurements by which it was found that saturable nonlinear absorption (light-induced transparency) and large negative nonlinear refraction were induced. We also measured dependences of the effective third- and fifth-order nonlinear refraction constants on CdSe QD volume fraction. Based on the Maxwell-Garnett model, we estimated the third- and fifth-order nonlinear optical susceptibilities of CdSe QD and discussed a contribution of the third-order effect to the fifth-order one due to the cascaded (local-field) effect. Coexistence of the third- and fifth-order nonlinear refraction was also confirmed by DMWM.