Investigation on sliding wear performance of WC10Co2Ni cladding developed through microwave irradiation

• Published in: Wear Vol. 271; no. 9; pp. 1642 - 1650
• Main Authors: Gupta, Dheeraj, Sharma, A.K.
• Format: Journal Article Conference Proceeding
• Language: English
• Published: Amsterdam Elsevier B.V 29-07-2011; Elsevier
• Subjects: Applied sciences; Austenitic stainless steels; Characterization; Cladding; Exact sciences and technology; Fracture mechanics (crack, fatigue, damage...); Friction, wear, lubrication; Frictional wear; Fundamental areas of phenomenology (including applications); Hybrid heating; Machine components; Mechanical engineering. Machine design; Microhardness; Microwave; Microwaves; Oxides; Physics; Scanning electron microscopy; Sliding friction; Sliding wear; Solid mechanics; Structural and continuum mechanics; WC10Co2Ni cladding; Wear resistance; Characterization; Microwave; Hybrid heating; WC10Co2Ni cladding; Sliding wear; Austenitic stainless steel; Vickers hardness; Hardness test; Scuffing; Thin film; Crack propagation; Wear resistance; Protective coatings; Pin disk test; Scanning electron microscopy; Adhesive wear; Oxide layer; Wear test; X ray radiography; Cladding; X ray diffraction; Microhardness; Stainless steel-316; Scaling; Porosity; Carbides; Crack; Tribology
• ISSN: 0043-1648; 1873-2577
• DOI: 10.1016/j.wear.2010.12.037

► Cermet cladding (WC10Co2Ni) developed using microwave heating. ► Dilution of material identified using electron microscopy and X-ray technique. ► Confirmed cermet cladding with composite characteristics. ► The approach appears suitable for producing crack and porosity free clads. ► Sliding wear resistance of the microwave clads has been evaluated.
Present work reports on the investigation of sliding wear of cladding developed through a novel processing technique. Wear resistant WC10Co2Ni cladding was developed using microwave irradiation on austenitic stainless steel (SS-316). The microwave claddings were characterized through field emission scanning electron microscope (FESEM), X-ray elemental analysis, X-ray diffraction (XRD) and measurement of Vicker′s microhardness. The FESEM study showed good metallurgical bond with substrate and the clads are free of cracks. Clads were formed with partial dilution of a thin layer of the substrate. The clad is composed of relatively soft metallic matrix and uniformly distributed hard carbide phase with ‘skeleton’ likes structure. The developed clads exhibit an average microhardness of 1064
±
99
Hv. The porosity of developed clad has been significantly less at approximately 0.89%. Tribological properties of cladding have been analyzed through pin on disc sliding method against an EN-31 (HRC-70) counter surface. The clads show significant resistance to sliding wear. Wear resistance was observed to be the better at lower sliding speeds. An unstable metallic oxide layer is formed during rubbing of clad surface. The loss of material from the mating surfaces is mainly due to spalling, growth of microcracks, and smearing of the unstable oxide layer.