Microstructural Coarsening Kinetics and Mechanical Property Changes in Long-Term Aged Sn–Pb–Sb Solder Joints by Susan, D. F., Wheeling, R. A., Williams, S. M., Yang, J., Jaramillo, C. E.

“…Tin-lead-antimony (50Sn–47Pb–3Sb wt.%) soldered assemblies were mechanically tested approximately 30 years after initial production and found to have solder…”
Get full text

Weldability testing to understand composition effects on eutectic backfilling in Ni-30Cr alloys by Wheeling, R. A., Lippold, J. C.

“…Using Ni-30 wt% Cr in nuclear power reactors requires compatible fillers to ensure reliable welded joints. The high chromium content provides resistance to…”
Get full text

Precipitation behavior and hardness response of Alloy 625 weld overlay under different aging conditions by Dai, T., Wheeling, R. A., Hartman-Vaeth, K., Lippold, J. C.

“…The hardness response of Alloy 625 weld overlay on low alloy steel was evaluated under a range of aging conditions to determine how the properties of the…”
Get full text

Effect of composition on grain boundary wetting characteristics in Ni-30Cr weld metal by Wheeling, R. A., Lippold, J. C.

“…The use of Ni-30Cr components in nuclear power reactors requires a compatible filler metal to ensure reliable welded joints associated with reactor vessels,…”
Get full text

Use of a Fracture Surface Cleaning Method to Evaluate Elevated Temperature Cracking in Steel by Wheeling, R. A., Lippold, J. C.

“…The nature of cracking during continuous casting of steel strip was investigated. Samples removed from steel strip for fractographic analysis were heavily…”
Get full text

Weldability testing to understand composition effects on eutectic backfilling in Ni-30Cr alloys by Wheeling, R. A., Lippold, J. C.