Search Results - "Holcomb, G. R."

Water Vapor Effects on the Oxidation Behavior of Fe–Cr and Ni–Cr Alloys in Atmospheres Relevant to Oxy-fuel Combustion by Mu, N., Jung, K. Y., Yanar, N. M., Meier, G. H., Pettit, F. S., Holcomb, G. R.

“…The oxidation behavior of a number of Fe–Cr- and Ni–Cr-based alloys was studied in atmospheres relevant to oxyfuel combustion at 650 °C. Oxidation was greatly…”
Get full text

Effect of SO2 on oxidation of metallic materials in CO2/H2O-rich gases relevant to oxyfuel environments by Huczkowski, P., Olszewski, T., Schiek, M., Lutz, B., Holcomb, G.R., Shemet, V., Nowak, W., Meier, G.H., Singheiser, L., Quadakkers, W.J.

“…In an oxyfuel plant, heat exchanging metallic components will be exposed to a flue gas that contains substantially higher contents of CO2, water vapor, and SO2…”
Get full text

Corrosion prevention and remediation strategies for reinforced concrete coastal bridges by Cramer, S.D, Covino, B.S, Bullard, S.J, Holcomb, G.R, Russell, J.H, Nelson, F.J, Laylor, H.M, Soltesz, S.M

“…Oregon's coastal highway includes over 120 bridges, most of which are reinforced concrete bridges. Twelve are historic structures. Over 40,000 m 2 of bridge…”
Get full text

Corrosion Failure of the Rocky Point Viaduct by Covino, B. S., Cramer, S. D., Holcomb, G. R., Bullard, S. J., Summers, C. A., Dahlin, C. L., Laylor, H. M., McGill, G. E.

“…The Rocky Point Viaduct, located near Port Orford, OR, was replaced after only 40 years of service. A beam from the original viaduct was studied in detail to…”
Get full text

Fireside Corrosion of Alumina-Forming Austenitic (AFA) Stainless Steels by Lutz, B. S., Yanar, N. M., Holcomb, G. R., Meier, G. H.

“…The performance of four alumina-forming austenitic alloys was tested in simulative fireside corrosion atmospheres. The alloys were exposed at 700 °C to gas…”
Get full text

Prevention of Chloride-induced Corrosion Damage to Bridges by Cramer, S. D., Covino, B. S., Jr, Bullard, S. J., Holcomb, G. R., Russell, J. H., Ziomek-Moroz, M., Virmani, Y. P., Butler, J. T., Nelson, F. J., Thompson, N. G.

“…The annual direct cost of bridge infrastructure corrosion to the U.S. economy is estimated at $8.3 billion, with indirect costs approximately 10 times higher…”
Get full text

The correlation between the new RigiScan plus software and the final diagnosis in the evaluation of erectile dysfunction by Benet, A E, Rehman, J, Holcomb, R G, Melman, A

“…The computer generated recordings for 2 nights in 40 patients studied with the RigiScan device were reevaluated using the new RigiScan Plus software to test…”
Get more information

Determination of the Initiation and Propagation Mechanism of Fireside Corrosion by Lutz, B. S., Holcomb, G. R., Meier, G. H.

“…A variety of deposit compositions were examined in short-term laboratory tests with the aim of determining the corrosion mechanisms of fireside corrosion for a…”
Get full text

Congenital pulmonary venous stenosis presenting as persistent pulmonary hypertension of the newborn by Holcomb, Robert G., Tyson, R. Weslie, Ivy, D. Dunbar, Abman, Steven H., Kinsella, John P.

“…Congenital pulmonary venous stenosis (CPVS) has been previously described in older infants and children, typically manifesting as failure to thrive with…”
Get full text

Failure analysis of an HCl gas cylinder valve by Holcomb, G.R

“…The fouling failure of an anhydrous HCl gas cylinder valve was investigated after the failure led to an accidental release of HCl gas. It is surmised that…”
Get full text

Bond Strength of Electrochemically Aged Arc-Sprayed Zinc Coatings on Concrete by Covino, B.S., Bullard, S.J., Holcomb, G.R., Cramer, S.D., McGill, G.E., Cryer, C.B.

“…ABSTRACTResearch was conducted to determine the effect of electrochemical aging on large-area arc-sprayed Zn anodes for cathodic protection (CP) of bridges and…”
Get full text

Humectant Use in the Cathodic Protection of Reinforced Concrete by Holcomb, G.R., Covino, B.S., Russell, J.H., Bullard, S.J., Cramer, S.D., Collins, W.K., Bennett, J.E., Laylor, H.M.

“…ABSTRACTUse of humectants to improve the thermal-sprayed zinc anode performance during the cathodic protection (CP) of reinforced concrete was examined. A…”
Get full text

Thermal sprayed titanium anode for cathodic protection of reinforced concrete bridges by CRAMER, S. D, COVINO, B. S, HOLCOMB, G. R, BULLARD, S. J, COLLINS, W. K, GOVIER, R. D, WILSON, R. D, LAYLOR, H. M

“…Stable operation of cobalt catalyzed thermal sprayed titanium anodes for cathodic protection (CP) of bridge reinforcing steel was maintained in accelerated…”
Get full text

Oxidation of hafnium carbide and hafnium carbide with additions of tantalum and praseodymium by COURTRIGHT, E. L, PRATER, J. T, HOLCOMB, G. R, ST. PIERRE, G. R, RAPP, R. A

“…The oxidation behavior of HfC, HfC-25 wt pct TaC, and HfC-7 wt pct PrC2 has been studied between 1200-2200 C. Parabolic growth of the oxide layer has been…”
Get full text

Hot corrosion in a temperature gradient by Holcomb, G. R.

“…Hot corrosion is the accelerated attack of materials at elevated temperatures that is induced by a thin film of fused salt. Many materials that experience hot…”
Get full text

Countercurrent Gaseous Diffusion Model of Oxidation Through a Porous Coating by Holcomb, G.R.

“…INTRODUCTIONMany materials have a solid and a gaseous oxidation product when oxidized. The solid product can grow at the solid-gas interface with a porous…”
Get full text

Fetal hepatic oxygen consumption under normal conditions in the fetal lamb by Holcomb, R G, Wilkening, R B

“…Previous measurements of fetal hepatic blood flow have relied on microsphere methodology. Estimates of fetal hepatic oxygen consumption (VO2), based on these…”
Get more information

Oxidation of CoCrFeMnNi High Entropy Alloys by Holcomb, Gordon R., Tylczak, Joseph, Carney, Casey

“…Eight model high entropy alloys (HEAs) in the CoCrFeMnNi family (including one alloy each in the CoCrFeNi and CoFeMnNi subfamilies) were made, prepared, and…”
Get full text

Report of a multicenter clinical evaluation of the Dura-II penile prosthesis by Kearse, Jr, W S, Sago, A L, Peretsman, S J, Bolton, J O, Holcomb, R G, Reddy, P K, Bernhard, P H, Eppel, S M, Lewis, J H, Gladshteyn, M

“…Information was collected during the first 2 years of an ongoing, prospective, multi-institutional evaluation of the Dura-II penile prosthesis. Evaluation…”
Get more information

The Effects of Water Vapor and Hydrogen on the High-Temperature Oxidation of Alloys by Mu, N., Jung, K., Yanar, N. M., Pettit, F. S., Holcomb, G. R., Howard, B. H., Meier, G. H.

“…Essentially all alloys and coatings that are resistant to corrosion at high temperature require the formation of a protective (slowly-growing and adherent)…”
Get full text