Behaviour of pre-stressed T91 and ODS steels exposed to liquid lead-bismuth eutectic by Hojna, Anna, Hadraba, Hynek, Di Gabriele, Fosca, Husak, Roman

“…[Display omitted] •Bend specimens were exposed to liquid lead-bismuth at 350°C up to 2000h.•Thin protective oxide layers; continuous on T91 and discontinuous…”
Get full text

Initiation of LME crack in ferritic martensitic steel in liquid lead-bismuth by Hojna, Anna, Di Gabriele, Fosca, Chocholousek, Michal, Spirit, Zbynek, Halodova, Patricie, Lorincik, Jan

“…This work is aimed at fundamental understanding of the T91 steel cracking mechanisms in liquid PbBi eutectic. In particular, the crack initiation was studied…”
Get full text

Effect of Applied Stress on T91 Steel Performance in Liquid Lead at 400 °C by Hojná, Anna, Di Gabriele, Fosca, Chocholoušek, Michal, Rozumová, Lucia, Vít, Jan

“…The environmental performance of structural materials (e.g., corrosion and environmental assisted cracking) is one of the critical issues being addressed in…”
Get full text

Behavior of the Steel T91 under Multi Axial Loading in Contact with Liquid and Solid Pb by Di Gabriele, Fosca, Hojna, Anna, Chocholousek, Michal, Klecka, Jakub

“…In this work, the conditions for the occurrence of Liquid Metal Embrittlement (LME) in the ferritic-martensitic steel T91 in contact with lead, Pb, were…”
Get full text

CHARACTERISATION OF OXIDES BY ADVANCED TECHNIQUES by Duchon, Jan, Halodova, Patricie, Lorincink, Jan, Di Gabriele, Fosca, Hojna, Anna

“…For the safe development of GenIV nuclear reactors, it is necessary to study the compatibility of structural materials with new coolants. The current work…”
Get full text

Fracture Resistance of 14Cr ODS Steel Exposed to a High Temperature Gas by Hojna, Anna, Michalicka, Jan, Hadraba, Hynek, Di Gabriele, Fosca, Duchon, Jan, Rozumova, Lucia, Husak, Roman

“…This paper studies the impact fracture behavior of the 14%Cr Oxide Dispersion Strengthened (ODS) steel (ODM401) after high temperature exposures in helium and…”
Get full text

Characteristics and Liquid Metal Embrittlement of the steel T91 in contact with Lead–Bismuth Eutectic by Hojna, Anna, Di Gabriele, Fosca, Klecka, Jakub

“…This paper summarizes results of the work carried out on the evaluation of the susceptibility to LME (Liquid Metal Embrittlement) of the ferritic/martensitic…”
Get full text

Mechanical properties of the steel T91 in contact with lead by Klecka, Jakub, Di Gabriele, Fosca, Hojna, Anna

“…•Tensile specimens of T91 steel were tested in liquid lead at 350°C and 400°C.•Several different fluxes were tested to promote wetting.•Liquid metal…”
Get full text

Behaviour of the steel T91 under uniaxial and multiaxial slow loading in contact with liquid lead by Hojná, Anna, Di Gabriele, Fosca, Klecka, Jakub, Burda, Jaroslav

“…This work deals with the interaction between liquid lead and the ferritic-martensitic steel, T91. Mechanical properties of specimens loaded in contact with…”
Get full text

Corrosion behaviour of 12Cr-ODS steel in molten lead by Di Gabriele, Fosca, Amore, Stefano, Scaiola, Celeste, Arato, Elisabetta, Giuranno, Donatella, Novakovic, Rada, Ricci, Enrica

“…•The corrosion of 12Cr-ODS steel was tested in static and flowing liquid lead.•The formation of external oxides and inner diffusion were observed.•In flowing…”
Get full text

Fracture behaviour of the 14Cr ODS steel exposed to helium and liquid lead by Hojna, Anna, Di Gabriele, Fosca, Hadraba, Hynek, Husak, Roman, Kubena, Ivo, Rozumova, Lucia, Bublikova, Petra, Kalivodova, Jana, Matejicek, Jiri

“…This work describes the fracture behaviour of the 14Cr ODS steel produced by mechanical alloying process, after high temperature exposures. Small specimens…”
Get full text

Metal dusting of nickel-base alloys by Di Gabriele, Fosca

“…Metal dusting is usually defined as catastrophic carburisation in conditions of high carbon activity and low oxygen partial pressure, in the temperature range…”
Get full text